Nimonic105 Material introduction

Nimonic105 It is a Ni Co Ci based precipitation hardening deformed superalloy, with the service temperature of 750 ℃ - 950 ℃. The alloy has high strength at room temperature and high temperature, good oxidation resistance, but general hot workability and welding performance. It is applicable to manufacturing high-temperature parts such as turbine blades and high-temperature bolts of aeroengines. The main products are hot rolled bars and flat products, cold drawn bars, profiles and rings.


Nimonic105 chemical composition

element

C

Cr

Ni

Co

Mo

Al

Ti

Fe

B

mass fraction/%

0.12-0.17

14.0-15.7

余

18.0-22.0

4.5-5.5

4.5-4.9

1.18-1.5

≤1.0

0.003-0.010

element

Mn

Si

P

S

Cu

Ag

Bi

Pb

Zr

mass fraction/%

≤0.40

≤0.25

≤0.015

≤0.01

≤0.200

≤0.0005

≤0.0001

≤0.0010

0.07-0.15


Nimonic105 Physical and mechanical properties

density

melting point

7.97g/cm³

1340-1380℃



varieties

heat treatment

σb/MPa

σp0.2/MPa

δ5/%

Cold drawn rod for bolts

Standard heat treatment

≥1000

≥680

≥18


Nimonic105 Heat treatment system

Hot rolled bars, flat products and forgings for blades, 1150 ℃± 10 ℃ * 4h/AC+1030 ℃± 10 ℃ * 16h/AC+700 ℃± 5 ℃ * 16h/AC;

Cold drawn rod, 1125 ℃± 10 ℃/AC+850 ℃± 10 ℃ * 16h/AC, including solution and heat preservation time：d≤3mm，1h；d>3mm-6mm，2h；d>6mm-40mm，4h。